具有聚集诱导发光性能的三苯甲醇侧基聚合物的制备及性能
作者:
作者单位:

作者简介:

通讯作者:

中图分类号:

基金项目:

国家科技重大专项课题(05Z12100010)


Synthesis and Properties of Aggregation-Induced-Emission Polymer with Pendant Triphenylmethanol Groups
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    通过Barbier反应合成了乙烯基三苯甲醇,其具有聚集诱导发光(AIE)现象;通过可逆加成-链转移(RAFT)聚合的方法将乙烯基三苯甲醇聚合得到不同相对分子质量的聚(三苯甲醇)乙烯。发现该聚合物表现出不同于小分子的AIE特性,在常温固态或溶液状态下均不产生荧光,但加热至玻璃化转变温度之后,聚合物固体的荧光发射强度明显增强,在溶液中依然不产生荧光。文中针对其特殊发光现象及发光机理进行了初步探究,通过核磁共振氢谱、红外光谱、X射线衍射与热力学表征发现其荧光的变化与激基缔合物有关。

    Abstract:

    Vinyl triphenyl methanol was synthesized by Barbier reaction, which shows aggregation-induced-emission (AIE) phenomenon. The polymers with different molecular weights were produced through reversible addition-chain transfer (RAFT) polymerization of vinyl triphenyl methanol. It is found that the polymer exhibit different AIE properties from its monomer and has no fluorescence at room temperature in both solid and solution states. However, after heating to its glass transition temperature, the fluorescence emission intensity of the solid polymer is significantly enhanced, and there is still no fluorescence in the polymer solution. In this paper, the special luminescence phenomenon and luminescence mechanism of the polymer were investigated. It is revealed that the fluorescence changes are related to the polymeric excimers by the characterization of NMR, IR, X-ray diffraction and thermodynamics.

    参考文献
    相似文献
    引证文献
引用本文

张晓云,贾会坤,叶 帆,刘江辉,张兆丽,吴 伟.具有聚集诱导发光性能的三苯甲醇侧基聚合物的制备及性能[J].高分子材料科学与工程,2020,36(1):1-5.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2020-02-26
  • 出版日期:
您是第位访问者
编辑出版:《高分子材料科学与工程》编辑部
地址:四川省成都市一环路南一段24号 四川大学高分子研究所
电话:028-8540 1653  E-mail:gfzclbjb@163.net; gfzclbjb@vip.sina.com
高分子材料科学与工程 ® 2022 版权所有
技术支持:北京勤云科技发展有限公司