以生物相容性微球为基质制备的接枝微球CPVA-g-PMAA对肌酐的吸附性能
DOI:
作者:
作者单位:

作者简介:

通讯作者:

中图分类号:

O631.3

基金项目:

山西省自然科学基金资助项目(2011021021-5)


Adsorption Property of Grafted Microspheres CPVA-g-PMAA Prepared with Biocompatible Microspheres as Matrix Towards Creatinine
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    在生物相容性微球交联聚乙烯醇(CPVA)微球表面实施甲基丙烯酸(MAA)的接枝聚合,制备了高接枝度(30g/100g)的接枝微球CPVA-g-PMAA。研究了接枝微球CPVA-g-PMAA对肌酐分子的吸附性能,分析了吸附机理。结果表明,在较大的pH范围内,CPVA-g-PMAA的Zeta电位为绝对值较大的负值。在强静电相互作用和氢键相互作用的协同下,CPVA-g-PMAA对肌酐分子表现出很强的吸附能力。随介质pH的增高,吸附容量先增大后减小,pH=8.0时,吸附容量最大(40mg/g);温度升高,吸附容量减小;CPVA-g-PMAA的接枝度增大,吸附容量升高。

    Abstract:

    Crosslinked polyvinyl alcohol(CPVA) microspheres are a class of polymer microspheres with biocompatibility.The surface-initiated graft polymerization of methacrylic acid(MAA) was performed,resulting in the grafted microspheres CPVA-g-PMAA with a high grafting degree(30g/100g).In this work,the adsorption behavior of the grafted microspheres CPVA-g-PMAA for creatinine was mainly investigated and the adsorption mechanism was explored.The experimental results show that in a wider pH range,the Zeta potential of the microspheres CPVA-g-PMAA is a negative value with a larger absolute value.By the driving of strong electrostatic interaction as well as by the synergism of hydrogen bond interaction,the grafted microspheres CPVA-g-PMAA display very strong adsorption ability for creatinine molecule.The adsorption capacity of the microspheres CPVA-g-PMAA for creatinine first increases and turns in decline with the increase of pH,and there is a maximum adsorption capacity of 40mg/g as pH=8.0.The adsorption capacity of the microspheres CPVA-g-PMAA for creatinine decreases with the increase of the temperature.The greater the grafting degree of the microspheres CPVA-g-PMAA is,the higher the adsorption capacity for creatinine is.

    参考文献
    相似文献
    引证文献
引用本文

张正国,高保娇,雷青娟.以生物相容性微球为基质制备的接枝微球CPVA-g-PMAA对肌酐的吸附性能[J].高分子材料科学与工程,2012,28(10):137-140.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 录用日期:
  • 网络出版日期:
  • 在线发布日期: 2013-04-16
  • 出版日期:
您是第      位访问者
编辑出版 :《高分子材料科学与工程》编辑部
地址 :四川省成都市一环路南一段24号 四川大学高分子研究所
电话 :028-8540 1653  E-mail:gfzclbjb@163.net; gfzclbjb@vip.sina.com
高分子材料科学与工程 ® 2024 版权所有
技术支持:北京勤云科技发展有限公司