预矿化丝素/壳聚糖复合支架的表征及细胞相容性
DOI:
作者:
作者单位:

作者简介:

通讯作者:

中图分类号:

基金项目:

国家现代农业产业技术体系专项(CARS-2Z-ZJ0402)


Characterization and Cytocompatibility of Premineralized Silk Fibroin/Chitosan Composite Scaffolds
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    以丝素和壳聚糖为原料,采用冷冻干燥法制备丝素/壳聚糖支架,通过预矿化使羟基磷灰石(HA)沉积,形成多孔羟基磷灰石-丝素蛋白/壳聚糖复合支架。对复合支架进行红外吸收光谱(FT-IR)、X 射线衍射(XRD)、扫描电子显微镜(SEM)、热重分析(TGA)、力学性能和空隙率表征;采用WST-1方法检测MG-63骨肉瘤细胞在复合支架上的增殖情况,评价其细胞相容性。结果显示,沉积的HA结构属于弱结晶态范畴,主要位于孔壁上,且随着预矿化循环次数的增加,沉积量增多,使预矿化复合支架的弹性模量得到极显著的提高,其孔隙率保持在90%左右的较高水平;WST-1检测表明,含有HA的预矿化复合支架对细胞增殖有明显的促进作用,具有良好的细胞相容性。

    Abstract:

    Silk fibroin/chitosan scaffolds were prepared through lyophilization, then hydroxyapatite was deposited by premineralization to obtain porous hydroxyapatite(HA)-silk fibroin/chitosan composite scaffolds.Composite scaffolds were characterized by Fourier transform infrared analysis(FT-IR), X-ray diffraction(XRD), scanning electronic microscopy(SEM), thermogravimetry analysis(TGA), compressive modulus and porosity,as well as the proliferation of MG-63 cells on composite scaffolds was detected by WST-1 method. The results reveal that the structure of deposited HA is a weak crystallinity, which deposits on the wall of pore. With the increase of premineralization cycles,the amount of HA and compressive modulus of premineralized composite scaffolds are significantly increased, the porosity keeps about 90%. WST-1 assay shows that premineralized composite scaffolds deposited with HA dramatically enhance the proliferation of cells, and possess a great cytocompatibility.

    参考文献
    相似文献
    引证文献
引用本文

施李杨, 邓连霞, 杨明英, 张海萍, Mandal Namita, 朱良均.预矿化丝素/壳聚糖复合支架的表征及细胞相容性[J].高分子材料科学与工程,2013,29(11):42-45.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 录用日期:
  • 网络出版日期:
  • 在线发布日期: 2013-11-11
  • 出版日期:
您是第      位访问者
编辑出版 :《高分子材料科学与工程》编辑部
地址 :四川省成都市一环路南一段24号 四川大学高分子研究所
电话 :028-8540 1653  E-mail:gfzclbjb@163.net; gfzclbjb@vip.sina.com
高分子材料科学与工程 ® 2024 版权所有
技术支持:北京勤云科技发展有限公司