Effect of Sequence Structure of NBR on Vulcanization Rate and Mechanical Properties
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    通过核磁共振技术(NMR)研究了丁腈橡胶中丙烯腈(AN)与丁二烯(BD)的序列结构对丁腈橡胶的硫化速率、拉伸性能的影响。结果表明,非极高腈品级丁腈橡胶的序列结构共有BAB、BBB、BBA/ABB、ABA4种;丙烯腈含量相同的丁腈橡胶的序列结构有很大的差异,且其硫化速率及力学性能受序列结构的影响很大。当BAB序列结构含量增加2.7%,焦烧时间缩短0.48min,拉伸强度增加2.34MPa,断裂伸长率增加80.52%。当BBB序列结构含量增加5.9%,正硫化时间缩短2.89min。

    Abstract:

    The effects of sequence structures of acrylonitrile (AN) and butadiene (BD) on the vulcanization rate and tensile properties of NBR were studied by NMR. The results show that there are four kinds of sequence structures of non-high grade nitrile NBR including BAB, BBB, BBA/ABB and ABA. The sequence structure of NBR with the same content of acrylonitrile is different, and its vulcanization rate and mechanical properties are greatly affected by the sequence structure. When the BAB sequence structure content is increased by 2.7%, the scorch time is decreased by 0.48 min, the tensile strength is increased by 2.34 MPa, and the elongation at break is increased by 80.52%. When the BBB sequence structure content is increased by 5.9%, the top optimum cure time is decreased by 2.89 min.

    参考文献
    相似文献
    引证文献
引用本文

陈昊诚,董瑞宝,王文玉,潘广勤.丁腈橡胶序列结构对其硫化速率及力学性能的影响[J].高分子材料科学与工程,2019,35(7):9-12.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 录用日期:
  • 网络出版日期:
  • 在线发布日期: 2019-08-09
  • 出版日期:
您是第      位访问者
编辑出版 :《高分子材料科学与工程》编辑部
地址 :四川省成都市一环路南一段24号 四川大学高分子研究所
电话 :028-8540 1653  E-mail:gfzclbjb@163.net; gfzclbjb@vip.sina.com
高分子材料科学与工程 ® 2024 版权所有
技术支持:北京勤云科技发展有限公司