Dynamic Rheological Behaviors and Temperature Dependence of Grated Polyethylene and Its Blends Based on Al-Plastic Tape Resins
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    制备马来酸酐接枝聚乙烯(LLDPE-g-MAH)/乙烯-丙烯酸共聚物(EAA)和马来酸酐接枝聚乙烯(LLDPE-g-MAH)/乙烯-醋酸乙烯酯共聚物(EVA)2种共混物,从共混物熔体的动态流变行为和温度依赖性两方面分析界面作用强度差异的原因。结果表明,LLDPE-g-MAH /EAA和LLDPE-g-MAH /EVA共混物作为黏合层,前者的剪切强度和剥离强度比后者高22.0 %和80.8 %;随着温度升高,前者的松弛指数(λ)先增加后减小,共混物的温度依赖性与LLDPE-g-MAH相一致,后者的松弛指数不受温度影响;LLDPE-g-MAH /EAA共混物的时温叠加(TTS)在整个频率区曲线完全不重合;后者的TTS曲线在高频区基本重合,低频区无法重合;前者的松弛时间逐渐缩短;后者的松弛时间与温度无关。

    Abstract:

    As communication cables, some reasons of difference on interface interaction between LLDPE-g-MAH/EAA and LLDPE-g-MAH/EVA were studied from dynamic rheological behaviors and temperature dependence. The results show that the shear strength and peel strength of LLDPE-g-MAH/EAA blends can meet national standards and increase by about 22.0 % and 80.8 % than those of LLDPE-g-MAH/EVA blends, respectively; the interfacial compatibility of LLDPE-g-MAH/EAA blends are better than LLDPE-g-MAH/EVA, with the temperature increasing, the relaxation index λ of LLDPE-g-MAH/EAA blends increases at first and then decreases, the temperature dependence of LLDPE-g-MAH/EAA are the same as one component LLDPE-g-MAH, the relaxation index λ of LLDPE-g-MAH/EVA blends is irrelevant to do with temperature; in the range of whole frequency, the time-temperature superposition (TTS)curves of LLDPE-g-MAH/EAA can not overlap,the TTS curves of LLDPE-g-MAH/EVA can overlap completely in the high frequency and can not overlap in low frequency. With the temperature increasing, the relaxation time of LLDPE-g-MAH/EAA reduces gradually, the relaxation time of LLDPE-g-MAH/EVA is irrelevant to do with temperature.

    参考文献
    相似文献
    引证文献
引用本文
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2021-07-19
  • 最后修改日期:2022-01-10
  • 录用日期:2022-03-25
  • 在线发布日期:
  • 出版日期:
您是第位访问者
编辑出版:《高分子材料科学与工程》编辑部
地址:四川省成都市一环路南一段24号 四川大学高分子研究所
电话:028-8540 1653  E-mail:gfzclbjb@163.net; gfzclbjb@vip.sina.com
高分子材料科学与工程 ® 2022 版权所有
技术支持:北京勤云科技发展有限公司