热处理工艺对玻纤增强聚酰胺66抗老化性能的影响
DOI:
作者:
作者单位:

山东科技大学 智能与装备学院,山东 泰安 271019

作者简介:

通讯作者:

中图分类号:

基金项目:

国家自然科学基金资助项目(51705295);国家自然科学基金资助项目(51778351);山东省自然科学基金重点项目(ZR2020KE013);山东科技大学科研基金项目(2018TDJH101);山东省高校青创科技计划(2019KJB015)


Effect of Hygrothermal Treatment Processes on Mechanical Properties and Microstructure of Hygrothermally Aged Glass Fiber Reinforced Polyamide 66
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    本文通过宏观力学性能测试和微观表征方法研究了不同热处理工艺对25wt.%短玻璃纤维(GF)增强PA66固定板抗老化性能的影响。将不同热处理工艺下的25wt.%GF/ PA66固定板放入恒温恒湿环境中(25℃,相对湿度70%),进行定期取样测试。分析结果表明,热处理温度对湿热老化时的吸湿增重率有明显的影响。20℃水煮温度处理比100℃在降低固定板吸水率、强度保持率以及硬度保持率方面均具有更好的效果;“靠模”的加入使得吸湿增重率有轻微下降,总体上有利于拉伸强度和弯曲强度的保持率。但“靠模”的加入使得硬度的数值和保持率均有轻微下降。通过扫描电镜观察弯曲断裂面可以证明四种热处理工艺下,试样在湿热老化后,玻璃纤维与PA66基体保持了良好的界面粘结强度。因此实验结果证明“靠模”+常温水煮对25wt.%GF/PA66固定板的吸湿增重率、拉伸强度、弯曲强度和硬度具有良好的保持效果,可有效地提高GF/PA66注塑制品的抗老化性能,这为玻纤增强PA66材料的抗湿热老化研究提供了借鉴和参考。

    Abstract:

    The effects of different hygrothermal treatment processes on the hygrothermal aging properties of 25 wt.% short glass fiber (GF)-reinforced polyamide 66(PA66) were investigated by macroscopic mechanical properties and microscopic characterization methods. The 25wt.% GF/ PA66 fixed plates with different hygrothermal treatment processes were put into the same hygrothermal aging environment for periodic sampling and testing, and the analysis results showed that the hygrothermal weight gain rate of fixed plates with different hygrothermal treatment processes decreased to different degrees. The mechanical properties test found that the hygrothermal treatment process improved the hygrothermal aging resistance of the fixed plate, and maintained high tensile and flexural strength and surface hardness in the hygrothermal aging environment; the temperature change of the hygrothermal treatment process had a greater impact on the decay of mechanical properties; the bending fracture surface was observed by scanning electron microscopy and it is found that after the hygrothermal treatment, the surface of the extracted fibers is covered with a large amount of resin matrix, and the cavities left by the extracted fibers at the fracture are also less, which indicates that the wet heat treatment can maintain good interfacial bond strength between the glass fibers and PA66 matrix of the specimen.

    参考文献
    相似文献
    引证文献
引用本文
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2022-03-29
  • 最后修改日期:2022-06-27
  • 录用日期:2022-07-19
  • 在线发布日期:
  • 出版日期:
您是第位访问者
编辑出版:《高分子材料科学与工程》编辑部
地址:四川省成都市一环路南一段24号 四川大学高分子研究所
电话:028-8540 1653  E-mail:gfzclbjb@163.net; gfzclbjb@vip.sina.com
高分子材料科学与工程 ® 2022 版权所有
技术支持:北京勤云科技发展有限公司